Alloy 825 Uns N08825 Plate

1. Material Grades: Incoloy 825, UNS N08825, W.NR. 2.4858
2. Width: 3.2~1500mm or as per your requirements
3. Thickness: 0.2~50mm or as per your requirements
{{0}} Length: 0~12m or as per your requirements

Ibgħat l-inkjesta

Introduzzjoni tal-Prodott

Incoloy 825 nickel-based alloy plate is the ultimate solution verified by the global industry. This is for complex corrosion and high temperature conditions, providing reliable protection for key equipment for more than ten years. HT PIPE is a Incoloy N08825 Plate supplier with 15+ export experience.

Specification of Incoloy 825 Plates

ASTM B424 / ASME SB424

1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc

2000mm, 2440mm, 3000mm, 5800mm, 8000mm, etc

0.3 mm to 120 mm

Coils, Foils, Rolls, Plain Sheet, Shim Sheet, Perforated Sheet, Chequered Plate, Strip, Flats, Blank (Circle), Ring (Flange) etc.

2B, 2D, BA, NO.1, NO.4, NO.8, 8K, mirror, Chequered, embossed, hair line, sand blast, Brush, etching, SATIN (Met with Plastic Coated) etc.

inco 825 chemical composition

	C			S
Incoloy 825	0.05 max	1.00 max	0.5 max	0.03 max	1.50 – 3.00	22.00 min	38.00 – 46.00	19.50 – 23.50	0.02 max	0.06 – 1.20

Grade 825 Incoloy ASTM B424 Sheets, Plates, Coils Mechanical Properties

				Yield Strength (0.2%Offset)
Incoloy 825	8.14 g/cm3	1400 ℃ (2550 ℃F)	Psi – 80,000 , MPa – 550	Psi – 32,000 , MPa – 220	30%

alloy 825 plate Corrosion protection

Chloride stress corrosion cracking (Cl-SCC) tolerance: the first choice for seawater pipelines on offshore platforms.
the corrosion rate in stagnant seawater is as low as 0.003 mm/a, which is almost "immune".
from boiling sulfuric acid, phosphoric acid to concentrated alkali solution (NaOH/KOH), the performance far exceeds that of 316L and other stainless steels.

n08825 material High temperature strength

It can serve for a long time at 550℃, has passed ASME boiler and pressure vessel certification, has a strength retention rate of over 80%, and has a creep rupture time of >5000 hours at 950℃, providing a "longevity gene" for high-temperature pipelines.